英语翻译Characterization:The AFM images were measuredwith SPA400 (Seiko Instruments Inc.) on new cleavedmica surface in tapping mode in air.The XRD patternswere obtained by using an X’Pert PRO MDP with Cu K radiation (\x08 1.5405 Å) with 3

英语翻译Characterization:The AFM images were measuredwith SPA400 (Seiko Instruments Inc.) on new cleavedmica surface in tapping mode in air.The XRD patternswere obtained by using an X’Pert PRO MDP with Cu K radiation (\x08 1.5405 Å) with 3
英语翻译
Characterization:The AFM images were measured
with SPA400 (Seiko Instruments Inc.) on new cleaved
mica surface in tapping mode in air.The XRD patterns
were obtained by using an X’Pert PRO MDP with Cu K
radiation (
\x08 1.5405 Å) with 30 mA and 40 kV.XPS
data were obtained with an ESCALab220i-XL electron
spectrometer from VG Scientific using 300 W Al K radiation.
The FT-IR spectrum was recorded by a Bruker
Equinox 55 FTIR spectrometer.The I\1V characteristics
of the cell were measured by an electrochemical analyzer
(CHI630A,Chenhua Instruments Co.,Shanghai) under
solar simulator illumination (CMH-250,Aodite Photoelectronic
Technology Ltd.,Beijing) at room
temperature.The IPCE was measured by illumination
with monochromatic light,which was obtained by a series
of light filters with different wavelengths.SEM images
were obtained using a JEOL JSM-6700F scanning
electron microscope at 3.0 kV.UV\1vis spectra were recorded
on a Hitachi Model U-4100 spectrophotometer.
The nitrogen adsorption and desorption isotherms at
the temperature of liquid nitrogen (77 K) were measured
on a Quantachrome Autosorb-1 sorption analyzer
with prior degassing under vacuum at 200 °C overnight.
Total pore volumes were determined using the
adsorbed volume at a relative pressure of 0.99.Multipoint
BET surface area was estimated from the relative
pressure range from 0.05 to 0.2.The pore size distribution
of the electrodes was analyzed using the BJH algorithm.
The EIS was carried out on a Zahner IM6e impedance
analyzer (Germany) in the frequency range of
0.02 Hz to 100 kHz with illumination of 100 mW/cm2.

英语翻译Characterization:The AFM images were measuredwith SPA400 (Seiko Instruments Inc.) on new cleavedmica surface in tapping mode in air.The XRD patternswere obtained by using an X’Pert PRO MDP with Cu K radiation (\x08 1.5405 Å) with 3
杜绝机译,最后的EIS什么意思吃不准
Characterization:The AFM images were measured with SPA400 (Seiko Instruments Inc.) on new cleaved mica surface in tapping mode in air.The XRD patterns were obtained by using an X’Pert PRO MDP with Cu K radiation ( 1.5405 Å) with 30 mA and 40 kV.
表征：原子力显微镜图像用SPA400（精工仪器公司）在空气中以间隔模式对新劈裂的云母表面测得.XRD（X射线衍射）图形用一台采用Cu（铜）K（钾）辐射（ 1.5405 Å)的X’Pert PRO MDP在30mA和40kV下获得.XPS data were obtained with an ESCALab220i-XL electron spectrometer from VG Scientific using 300 W Al K radiation.XPS（X射线光电子分光术）数据用产自VG Scientific公司的ESCALab220i-XL 电子能谱仪,采用300W Al（铝）K(钾)辐射获得.The FT-IR spectrum was recorded by a Bruker Equinox 55 FTIR spectrometer.FT-IR （傅立叶变换－红外）光谱用一台Bruker Equinox 55 FTIR分光仪记录.The I V characteristics of the cell were measured by an electrochemical analyzer (CHI630A,Chenhua Instruments Co.,Shanghai) under solar simulator illumination (CMH-250,Aodite Photoelectronic Technology Ltd.,Beijing) at room temperature.Cell（电池）的IV特性用一台电化学分析仪（CHI630A,上海辰华仪器有限公司出产）在
室温太阳模拟器照明（北京Aodite光电子科技有限公司的CMH- 250）下进行测量.The IPCE was measured by illumination with monochromatic light,which was obtained by a series of light filters with different wavelengths.IPCE（光电转化效率）通过用单色光照射来测量,此单色光由一系列的不同波长的滤光器得到.SEM images were obtained using a JEOL JSM-6700F scanning electron microscope at 3.0 kV.扫描电镜图像用伊泰JEOL JSM-6700F扫描电子显微镜在3.0kV下获得.UV vis spectra were recorded on a Hitachi Model U-4100 spectrophotometer.紫外可见光谱在日立Model U-4100 分光光度计上记录.The nitrogen adsorption and desorption isotherms at the temperature of liquid nitrogen (77 K) were measured on a Quantachrome Autosorb-1 sorption analyzer with prior degassing under vacuum at 200 °C overnight.在液氮（77K）温度下的氮吸收和解吸收等温线在伊泰Quantachrome Autosorb-1吸附分析仪上测量,事先要在200 °C 的真空下脱气过夜.Total pore volumes were determined using the adsorbed volume at a relative pressure of 0.99.总的空隙体积用0.99相对压力下的吸附体积来确定.Multipoint BET surface area was estimated from the relative pressure range from 0.05 to 0.2.多点BET比表面积由从0.05到0.2的相对压力范围估算.The pore size distribution of the electrodes was analyzed using the BJH algorithm.电极的空隙尺寸分布用BJH算法分析.The EIS was carried out on a Zahner IM6e impedance analyzer (Germany) in the frequency range of 0.02 Hz to 100 kHz with illumination of 100 mW/cm2.EIS在一台Zahner IM6e阻抗分析仪（德国产）上,在0.02Hz到100kHz的频率范围内通过100mW/cm2的照射来进行.

Characterization: The AFM images were measured
AFM图像表征:测量
with SPA400 (Seiko Instruments Inc.) on new cleaved
与SPA400。)(精工仪器公司)在新裂
mica surface in tapping mode in air. The XRD patter...

全部展开

Characterization: The AFM images were measured
AFM图像表征:测量
with SPA400 (Seiko Instruments Inc.) on new cleaved
与SPA400。)(精工仪器公司)在新裂
mica surface in tapping mode in air. The XRD patterns
在云母表面敲击模式在空气中。射线衍射模式
were obtained by using an X’Pert PRO MDP with Cu K
利用X取得了'Pert箴躁郁与铜K
radiation (
辐射(
1.5405 Å) with 30 mA and 40 kV. XPS
一)和30 1.5405马和40千伏。XPS
data were obtained with an ESCALab220i-XL electron
获得了有关数据与一个ESCALab220i-XL电子
spectrometer from VG Scientific using 300 W Al K radiation.
科学使用VG光谱仪300 W铝K辐射。
The FT-IR spectrum was recorded by a Bruker
傅立叶变换红外光谱的Bruker记录
Equinox 55 FTIR spectrometer. The IV characteristics
FTIR光谱仪春分55岁。第四特点
of the cell were measured by an electrochemical analyzer
测量了细胞的电化学分析仪
(CHI630A, Chenhua Instruments Co., Shanghai) under
(CHI630A仪器有限公司,上海,Chenhua)下的
solar simulator illumination (CMH-250, Aodite Photoelectronic
太阳模拟器,Aodite(CMH-250光电照明
Technology Ltd., Beijing) at room
科技有限公司、北京)在房间里
temperature. The IPCE was measured by illumination
温度。测量了IPCE照明
with monochromatic light, which was obtained by a series
以单色的光,并得出一个系列
of light filters with different wavelengths. SEM images
光的过滤器,不同的波长。SEM分析
were obtained using a JEOL JSM-6700F scanning
使用JEOL取得了JSM-6700F扫描吗
electron microscope at 3.0 kV. UVvis spectra were recorded
电子显微镜在3.0千伏。UVvis光谱进行记录
on a Hitachi Model U-4100 spectrophotometer.
日立模型上U-4100分光光度计。
The nitrogen adsorption and desorption isotherms at
氮吸附和解吸静态吸附等温线
the temperature of liquid nitrogen (77 K) were measured
液氮温度(77 K)量
on a Quantachrome Autosorb-1 sorption analyzer
Autosorb-1吸附在Quantachrome分析仪
with prior degassing under vacuum at 200 °C overnight.
真空脱气与之前在200°C过夜。
Total pore volumes were determined using the
总孔隙体积的分析,确定了使用
adsorbed volume at a relative pressure of 0.99. Multipoint
在一个相对压力吸附量的订正。多点
BET surface area was estimated from the relative
表面积是估计的相对的
pressure range from 0.05 to 0.2. The pore size distribution
压力范围从0.05 ~ 0.2。孔隙大小分布
of the electrodes was analyzed using the BJH algorithm.
分析了将电极的使用BJH算法。
The EIS was carried out on a Zahner IM6e impedance
三星的一个Zahner进行了IM6e阻抗
analyzer (Germany) in the frequency range of
分析仪(德国)的频率范围
0.02 Hz to 100 kHz with illumination of 100 mW/cm2.
0.02赫兹到100千赫与光照100兆瓦/平方厘米。

收起

AFM图像表征:测量
与SPA400。)(精工仪器公司)在新裂
在云母表面敲击模式在空气中。射线衍射模式
利用X取得了'Pert箴躁郁与铜K
辐射(
一)和30 1.5405马和40千伏。 XPS
获得了有关数据与一个ESCALab220i-XL电子
科学使用VG光谱仪300 W铝K辐射。
傅立叶变换红外光谱的Bruker记录

全部展开

AFM图像表征:测量
与SPA400。)(精工仪器公司)在新裂
在云母表面敲击模式在空气中。射线衍射模式
利用X取得了'Pert箴躁郁与铜K
辐射(
一)和30 1.5405马和40千伏。 XPS
获得了有关数据与一个ESCALab220i-XL电子
科学使用VG光谱仪300 W铝K辐射。
傅立叶变换红外光谱的Bruker记录
FTIR光谱仪春分55岁。第四特点
测量了细胞的电化学分析仪
(CHI630A仪器有限公司,上海,Chenhua)下的
太阳模拟器,Aodite(CMH-250光电照明
科技有限公司、北京)在房间里
温度。测量了IPCE照明
以单色的光,并得出一个系列
光的过滤器,不同的波长。SEM分析
使用JEOL取得了JSM-6700F扫描吗
电子显微镜在3.0千伏。UVvis光谱进行记录
日立模型上U-4100分光光度计。
氮吸附和解吸静态吸附等温线
液氮温度(77 K)量
Autosorb-1吸附在Quantachrome分析仪
真空脱气与之前在200°C过夜。
总孔隙体积的分析,确定了使用
在一个相对压力吸附量的订正。多点
表面积是估计的相对的
压力范围从0.05 ~ 0.2。孔隙大小分布
分析了将电极的使用BJH算法。
三星的一个Zahner进行了IM6e阻抗
分析仪(德国)的频率范围
0.02赫兹到100千赫与光照100兆瓦/平方厘米。