As is clear from the nature of the process,a key factor in determining the amount of final shrinkage is the unit water content of the fresh concrete.This isillustrated in Fig 2.9,which shows the amount of shrinkage foe varying amountsof mixing water.This very large variation of cement content causes a 20 to 30percent variation in shrinkage strain for water contents between 250 to 350lb/y .the range used for most structuralconcretes.Increasing the cement content increases he cement paste constituentof the concrete,where the shrinkage actually takes places,while reducing theaggregate the content can significantly decrease shrinkage.This is shown inFig 2.10,which compares the shrinkage of concretes with various aggregatecontent with the shrinkage obtained forneat cement (cement and water alone).For example,increasing the aggregatecontent from 71 to 74 percent (at the same water –cement ratio) result in a 20percent reduction in shrinkage(Ref 2.24).Increases aggregate
Content may beobtained through the use of (1) a large maximum size coarse aggregate(whichalso reduces the content required for a given workability),(2) a concrete withlower workability,and(3) chemical admixtures to increase workability at areduction in water content and an increase in aggregate content.In addition,prolonged and careful curing is beneficial for shrinkage control.
英语翻译As is clear from the nature of the process,a key factor in determining the amount of final shrinkage is the unit water content of the fresh concrete.This isillustrated in Fig 2.9,which shows the amount of shrinkage foe varying amountsof m
附件中仅是英文,涂红处,请你再看一下,我实在看不懂,待你看后,如需翻译,你再追问.如有其它网友做妥,我就不必再翻了.
从这个过程的本质是明确的,在确定最终的收缩量的一个关键因素是新拌混凝土的单位用水量。这说明了在图2.9,这表明收缩变的混合水的量。这个非常大的变化,导致水泥含量20~30%变化的收缩应变的水分含量在250的成绩是
用于大多数structuralconcretes范围。提高水泥含量的增加,他水泥浆体组成部分混凝土在收缩,其实需要的地方,同时降低聚合内容可显著降低收缩。这是示图2.10,比较了...
全部展开
从这个过程的本质是明确的,在确定最终的收缩量的一个关键因素是新拌混凝土的单位用水量。这说明了在图2.9,这表明收缩变的混合水的量。这个非常大的变化,导致水泥含量20~30%变化的收缩应变的水分含量在250的成绩是
用于大多数structuralconcretes范围。提高水泥含量的增加,他水泥浆体组成部分混凝土在收缩,其实需要的地方,同时降低聚合内容可显著降低收缩。这是示图2.10,比较了不同骨料含量与收缩得到forneat水泥混凝土的收缩(水泥和水)。例如,在骨料含量从71增加到百分之74(在相同的水灰比在–)收缩减少20%的结果(参考文献2.24)。增加骨料内容可能获得通过使用(1)大最大骨料(同样减少了对于一个给定的性能要求的内容),(2)混凝土和易性,及(3)化学外加剂提高加工性在减少水含量和骨料含量的增加。此外,长期的和精心的养护有利于收缩控制
收起
谁写的垃圾文章啊,搞的这么文绉绉的,本来简简单单就可以写出来的英文,搞的和报告一样,鄙视~
可以很清楚的从大自然的过程中,一个关键的因素在确定数量的最终收缩是单位含水量的新鲜混凝土。这isillustrated在图2.9,显示了数量的收缩敌人不同巨大拌和水。这非常大的变化,会导致水泥含量30%到的收缩应变变化对水含量在250至350磅/ y。用于大多数structuralconcretes范围。增加水泥含量增加他constituentof混凝土水泥浆,收缩实际上需要的地方,同时减少the...
全部展开
可以很清楚的从大自然的过程中,一个关键的因素在确定数量的最终收缩是单位含水量的新鲜混凝土。这isillustrated在图2.9,显示了数量的收缩敌人不同巨大拌和水。这非常大的变化,会导致水泥含量30%到的收缩应变变化对水含量在250至350磅/ y。用于大多数structuralconcretes范围。增加水泥含量增加他constituentof混凝土水泥浆,收缩实际上需要的地方,同时减少theaggregate内容可以显著减少收缩。这是inFig显示2.10,比较了各种aggregatecontent混凝土收缩和收缩获得forneat水泥(水泥和水单)。例如,增加aggregatecontent从71到74%(在同一水灰比)减少20%的收缩(参考2.24)。增加骨料
beobtained内容可以通过使用(1)一个大最大尺寸粗骨料(whichalso减少所需的内容对于一个给定的可加工性),(2)一个具体的withlower和易性,(3)化学外加剂在areduction增加和易性在水含量和增加聚合内容。此外,长期和细心养护有利于收缩控制
收起