介绍通过调整反应温度、反应时间、抗菌剂中银、锌离子的含量，研究载银锌沸石抗菌剂的稳定性和抗变色性，并对其抗变色性能和抗菌性能进行了测试和分析。得出载银锌沸石的最佳制备环境为使用0.1mol/L的AgNO3溶液和2mol/L的ZnSO4溶液进行混合在70℃的水浴锅中搅拌3小时。本文还采用抑菌环和抑菌率实验对最佳环境下制备载银锌沸石抗菌剂涂布抗菌包装纸的抗菌性能和物理性能进行了测定与研究。结果表明，减少载银锌沸石抗菌剂中银离子的含量，增加锌离子的含量，抗菌剂样品的抗菌性能变化不大，而抗变色性能却有较大提升。
使用该方法制备的载银锌沸石抗菌剂稳定性较好，避光保存时间较长，杀菌性能较好，抗变色性优良，是载银沸石的理想替代品。
关键词：抗菌材料；载银锌沸石；抑菌环测试；抗菌纸

英语翻译介绍通过调整反应温度、反应时间、抗菌剂中银、锌离子的含量，研究载银锌沸石抗菌剂的稳定性和抗变色性，并对其抗变色性能和抗菌性能进行了测试和分析。得出载银锌沸石的
Introduced by adjusting the reaction temperature, reaction time, antimicrobial agents silver and zinc ion content of antimicrobial silver zinc zeolite stability and anti-tarnish resistance, and its anti-tarnish properties and antibacterial properties were tested and analyzed. Silver zinc zeolite obtained the best preparation for the use of environment 0.1mol / L of the AgNO3 solution and 2mol / L of ZnSO4 solution was mixed in the mixing pot 70 ℃ water bath for 3 hours. This article also inhibitory rate by inhibition zone and the best experimental conditions for preparation of silver zinc coated zeolite antibacterial antibacterial agents antibacterial properties of wrapping paper and physical properties were determined and research. The results showed that the reduction of silver zeolite antimicrobial agent in the zinc content of silver ions to increase the zinc content of the antimicrobial properties of antimicrobial little change in the sample, and anti-tarnish performance there is much improvement.
Prepared using the method of antimicrobial silver zinc zeolite stability is good, dark storage time is longer, better bactericidal properties, excellent resistance to discoloration, silver zeolite is an ideal substitute.
Key words: antibacterial materials; containing silver-zinc zeolite; inhibition zone test; Antibacterial Paper

The introduction through the adjustment reaction temperature, the reaction time, antibiotics Bank of China, the zinc ion content, the research carries the silver zinc zeolite antibiotics the stability...

全部展开

The introduction through the adjustment reaction temperature, the reaction time, antibiotics Bank of China, the zinc ion content, the research carries the silver zinc zeolite antibiotics the stability and the anti-color change, and has carried on the test and the analysis to its anti-color deterioration performance and the antibacterial performance. Obtains carries the silver zinc zeolite the best preparation environment to use 0.1mol/L the AgNO3 solution and the 2mol/L ZnSO4 solution carries on the mix in 70℃ in the water-bath to stir for 3 hours. This article also used damps the ring and the bacteriostasis rate experiment the system publishes a detailed explanation the silver zinc zeolite antibiotics to the best environment under to spread the cloth antibacterial packing paper the antibacterial performance and the physical property has carried on the determination and the research. The result indicated that reduces carries the silver zinc zeolite antibiotics Bank of China ion the content, increases the zin

收起

Introduction by adjusting the reaction temperature, reaction time, antibacterial agent boc, zinc ion content, research load silver zinc zeolite antibacterial agent of stability and resistance to color...

全部展开

Introduction by adjusting the reaction temperature, reaction time, antibacterial agent boc, zinc ion content, research load silver zinc zeolite antibacterial agent of stability and resistance to color, and the resistance of discolouration performance and antibacterial properties were tested and analyzed. Draw the best contained silver zinc zeolite preparation for the use of 0.1 mol/environment of AgNO3 solution and L 2mol/L ZnSO4 solution mixed in 70 ℃ stir the pot water-bath three hours. This paper also using bacteriostatic annulus and bacteriostasis rate for the best environment experiment preparation load silver zinc zeolite antiseptics coating antibacterial wrapping paper antibacterial properties and physical properties of determination and research. The results show that reduce load silver zinc zeolite antiseptics boc ion content and increase the content of zinc ions, antibacterial agent samples little change, and antimicrobial resistance performance has a larger discoloration of ascension.

收起