一段英语文献翻译To gain further information about the active compounds of 0.01%Pt–0.02%Pd/stainless steel catalyst before and after 800 h reaction, ICP measurement was used to characterize the samples. As shown in Table 2, the da
来源:学生作业帮助网 编辑:六六作业网 时间:2024/11/24 19:40:27
一段英语文献翻译To gain further information about the active compounds of 0.01%Pt–0.02%Pd/stainless steel catalyst before and after 800 h reaction, ICP measurement was used to characterize the samples. As shown in Table 2, the da
一段英语文献翻译
To gain further information about the active compounds of 0.01%Pt–0.02%Pd/stainless steel catalyst before and after 800 h reaction, ICP measurement was used to characterize the samples. As shown in Table 2, the data shows nearly no decrease in the content of the catalyst active compounds, which indicates the 0.01%Pt–0.02%Pd/ stainless steel catalyst, is stable, even in such a long reaction time. 化工的,哪位朋友亲自帮我翻译下,O(∩_∩)O谢谢
一段英语文献翻译To gain further information about the active compounds of 0.01%Pt–0.02%Pd/stainless steel catalyst before and after 800 h reaction, ICP measurement was used to characterize the samples. As shown in Table 2, the da
为了进一步获取有关0.01%Pt-0.02%Pd 不锈钢催化剂的活化物在800小时反应前后的数据,我们使用ICP测量方法对样本进行了分析.表2的数据表明,催化剂的活性成份几乎没有任何的减少.这表明,即便经过这样长时间的反应,0.01%Pt-0.02%Pd /不锈钢催化剂也是稳定.
为获得更多800小时反应前后有关0.01%Pt-0.02%Pd 不锈钢催化剂活性化合物的信息,我们使用了ICP测量来描述样本。数据表明,催化剂的活性成份几乎没有减少。这表明,即使经过这样长的反应时间,0.01%Pt-0.02%Pd /不锈钢催化剂是稳定。见表2。
为了获得0.01%Pt-0.02%Pd/不锈钢催化剂上活泼化合物反应800小时前后的更多信息,用ICP来表征催化剂样品。如表2所示,催化剂上活泼化合物几乎没有减少,这表明0.01%Pt-0.02%Pd/不锈钢催化剂即使在反应很长时间也很稳定,。
获得更多的信息的活性化合物的0.01%Pt-0.02%Pd .不锈钢催化剂反应前后,威达电800小时测量用于表征样本。表2中所示的数据显示,在内容上几乎没有减少催化剂的活性化合物,既体现了0.01%Pt-0.02%Pd /不锈钢催化剂,是稳定的,即使在这样一个长反应时间。
获得更多的信息的活性化合物的0.01%Pt-0.02%Pd /不锈钢催化剂反应前后,威达电800小时测量用于表征样本。表2中所示的数据显示,在内容上几乎没有减少催化剂的活性化合物,既体现了0.01%Pt-0.02%Pd /不锈钢催化剂,是稳定的,即使在这样一个长反应时间。怎么大家都一样啊....