Pd catalysts supported on activated carbon felts (ACFs) with different metallic loadings were prepared by electroless
plating and evaluated for the reduction of nitrite in water in a batch reactor. Homogeneous Pd dispersions
were obtained, the plating solution concentration and the seeding step being the key variables that determine
particle size and morphology. The formation of Pd crystals of 96±22 nm situated at the external surface of
the carbon fibers was obtained for 0.14 wt.% of metal loading, while an incipient formation of a Pd thin layer
was detected for 1.9 wt.%. The fresh and used catalysts were characterized by SEM, EDS, XRD and XPS.

求翻译 化学镀Pd catalysts supported on activated carbon felts (ACFs) with different metallic loadings were prepared by electrolessplating and evaluated for the reduction of nitrite in water in a batch reactor. Homogeneous Pd dispersionswere obt
在活性碳毡负载Pd催化剂（ACF）与不同金属负载量的化学镀和评价为减少在间歇反应器中亚硝酸盐的制备.dispersionswere获得均匀的Pd,镀液浓度和播种的步骤,determineparticle尺寸和形貌的关键变量.得到的0.14重量%的金属负载量为96±22 nm处的外表面的碳纤维钯晶体的形成,而钯薄膜层检测早期形成1.9重量%.新鲜的和使用的催化剂进行了表征SEM,EDS,XRD和XPS.
绝对正确

活性炭毡 (用活性炭纤维) 与不同金属荷载钯催化剂化学镀的编制，并进行评估，减少的亚硝酸盐在水中搅拌反应器中反应。获得的均质 Pd dispersionswere、 电镀溶液的浓度和正在的关键变量，determineparticle 大小和形态的播一步。位于外部表面照射碳纤维 96±22 nm 的 Pd 晶体的形成被获得 0.14 wt.%金属加载，虽然初期形成的 Pd 薄 layerwas 1....

全部展开

活性炭毡 (用活性炭纤维) 与不同金属荷载钯催化剂化学镀的编制，并进行评估，减少的亚硝酸盐在水中搅拌反应器中反应。获得的均质 Pd dispersionswere、 电镀溶液的浓度和正在的关键变量，determineparticle 大小和形态的播一步。位于外部表面照射碳纤维 96±22 nm 的 Pd 晶体的形成被获得 0.14 wt.%金属加载，虽然初期形成的 Pd 薄 layerwas 1.9 wt.%为检测到。SEM、 EDS、 XRD 和 XPS 的特点是新鲜和使用催化剂。

收起

用化学镀的方法获得了不同含量的形态均匀的沉积在活性炭毡上的具有催化活性的金属钯，用于测试间歇反应器中亚硝酸根的还原性。镀液的浓度、晶种的形成步骤是决定金属钯的颗粒大小和形态的关键。钯种在碳毡外表面，当颗粒大小是96±22 nm时的含量是0.14 wt.% （重量百分比），而当形成金属钯薄层时，含金属钯的量达到了1.9 wt.%。用SEM, EDS, XRD 和 XPS方法对试验前、试验后的碳毡进行...

全部展开

用化学镀的方法获得了不同含量的形态均匀的沉积在活性炭毡上的具有催化活性的金属钯，用于测试间歇反应器中亚硝酸根的还原性。镀液的浓度、晶种的形成步骤是决定金属钯的颗粒大小和形态的关键。钯种在碳毡外表面，当颗粒大小是96±22 nm时的含量是0.14 wt.% （重量百分比），而当形成金属钯薄层时，含金属钯的量达到了1.9 wt.%。用SEM, EDS, XRD 和 XPS方法对试验前、试验后的碳毡进行了表征。.