英语翻译3 Results and DiscussionIn this article,the effects of FA,GBS and SF used in LC both respectively and together on the permeability were studied.The results are shown in Table 3,the more the quantity that passed through the specimen and th

英语翻译3 Results and DiscussionIn this article,the effects of FA,GBS and SF used in LC both respectively and together on the permeability were studied.The results are shown in Table 3,the more the quantity that passed through the specimen and th
英语翻译
3 Results and Discussion
In this article,the effects of FA,GBS and SF used in LC both respectively and together on the permeability were studied.The results are shown in Table 3,the more the quantity that passed through the specimen and the higher the height of water penetration of concrete,the lower the anti-permeability of concrete.As shown in the form,the results get from two kinds of experiment methods have unanimous laws.As shown in Table 3,by comparing the electric conduction quantity of specimen 1#with that of specimen0#,it is easy to find that both LC60 and NC60 have a rather good anti-permeability.However,under the same strength grade condition,the permeability of LC is greater than that of NC.By comparing the chloride permeation coefficient and the height of water penetration of specimen1#with those of 2#,3#,4#,5#,it is apparent that the antipermeability of LC can be significantly improved by utilizing FA and SF respectively,especially the specimen 4#in which 10% cement was replaced by SF gets the best anti-permeability performance.Its chloride permeation coefficient is only 4.6×10-9cm2/s and the height of water penetration is only 10.1mm.Though the electric conduction quantity of specimen 3#inwhich 10% cement was replaced by GBS is smaller than that of 1#,which is a control sample,it is apparently larger than that of 2#,indicating that the improved effect of GBS on antipermeability of concrete is inferior to that of FA,while that of FA and GBS applied together to replace 10% cement respectively (specimen 5#) is much more notable.

英语翻译3 Results and DiscussionIn this article,the effects of FA,GBS and SF used in LC both respectively and together on the permeability were studied.The results are shown in Table 3,the more the quantity that passed through the specimen and th
3结果与讨论
在这篇文章中,影响发, gbs和SF用在立法会都分别和共同对渗透率进行了研究.结果表3所示,更多数量通过标本和更高的高度,透水混凝土,降低抗渗混凝土.显示,在形式,结果得到的两种实验方法有一致的法律.如表3所示,通过比较导电量的标本1 ＃与的specimen0编号,很容易找到双方lc60和nc60有一个相当良好的抗渗透性.不过,根据同一强度等级的条件下,透气性立法会大于数控加工.通过比较氯化渗透系数和高度的水渗透specimen1 ＃与2 ＃ , 3 ＃ , 4 ＃ , 5 ＃ ,很明显,该antipermeability立法会可显着改善,利用发和SF分别,尤其是该标本4 ＃ ,其中10 ％的水泥所取代,证券及期货得到最好的抗渗性能.其氯离子渗透系数只有4.6 × 10 - 9平方厘米/ S和高度渗水只是10.1mm.though电传导的数量,标本3 ＃ inwhich 10 ％ ,水泥取代gbs是小于1 ＃ ,是一个控制样本,这是很明显大于2 ＃ ,表明该改进的效果GBS的对antipermeability混凝土是劣,即发,而FA旱地龙和gbs应用一起,以取代10 ％ ,水泥分别为（标本5 ＃ ）是更为显着.