英语翻译XRD and XPS.The X-ray powder diffraction patternsof the AgI/BiOI composites with different AgI amounts areshown in Figure 1.It is observed that all the peaks of the pureBiOI sample (Figure 1a) coincide with the standard tetragonalBiOI pha

来源：学生作业帮助网编辑：六六作业网时间：2024/11/24 05:24:35

英语翻译XRDandXPS.TheX-raypowderdiffractionpatternsoftheAgI/BiOIcompositeswithdifferentAgIamountsareshow

英语翻译XRD and XPS.The X-ray powder diffraction patternsof the AgI/BiOI composites with different AgI amounts areshown in Figure 1.It is observed that all the peaks of the pureBiOI sample (Figure 1a) coincide with the standard tetragonalBiOI pha
英语翻译
XRD and XPS.The X-ray powder diffraction patterns
of the AgI/BiOI composites with different AgI amounts are
shown in Figure 1.It is observed that all the peaks of the pure
BiOI sample (Figure 1a) coincide with the standard tetragonal
BiOI phase (JCPDS No.73-2062).The peaks of AgI become
broaderwith the increase of AgI amount,indicating that the grain
sizes decrease.The identification of the XRD patterns of AgI
(Figure 1f ) demonstrates that it can be indexed to be the
hexagonal β-AgI phase (JCPDS No.09-0374),27 and no other
AgI phases are found.In addition,from the diffraction patterns
(Figure 1b-e),we can clearly see that all theAgI/BiOI composites
exhibit a coexistence of both AgI and BiOI phases.

英语翻译XRD and XPS.The X-ray powder diffraction patternsof the AgI/BiOI composites with different AgI amounts areshown in Figure 1.It is observed that all the peaks of the pureBiOI sample (Figure 1a) coincide with the standard tetragonalBiOI pha
图一是AgI/BiOI 复合物中AgI的含量不同的XRD图谱.据观察,所有峰的纯BiOI样本（图1a）与标准的四方相BiOI相符（JCPDS73-2062号）.碘化银的峰随着AGI量的增加变得更宽,这表明晶体颗粒尺寸减小.碘化银的XRD图谱分析（图1F）表明,它可以被标示是六角相的β-AGI（JCPDS09-0374号）,没有其他碘化银相被发现.此外,从衍射图（图1b-e）,我们可以清楚地看到,所有AgI/ BiOI以AgI 和 BiOI 二种相态混合共存.
(ps)这其中要深入了解查询卡片号请安装软件jade5.0,同时为什么峰型变宽,晶粒直径变小,这个请查询谢乐公式.

XRD和XPS。
AGI/ BiOI的X-射线粉与不同的碘化银混合
衍射图样
如图1所示。

全部展开

XRD和XPS。 AGI/ BiOI的X-射线粉末衍射图样
与不同的碘化银混合
如图1所示。据观察，所有峰的纯
BiOI样本（图1a）与标准的四方相
BiOI相符（JCPDS73-2062号）。碘化银的峰更广泛
随着AGI量的增加，这表明颗粒
尺寸减小。碘化银的XRD图谱鉴定
（图1F）表明，它可以被标示是
六角相的β-AGI（JCPDS09-0374号），27，没有其他
碘化银阶段被发现。此外，从衍射图
（图1b-E），我们可以清楚地看到，所有theAgI/ BiOI混合
呈现共存双方碘化银和BiOI的阶段。
翻译不同意啊，望采纳

收起

英语翻译XRD and XPS.The X-ray powder diffraction patternsof the AgI/BiOI composites with different AgI amounts areshown in Figure 1.It is observed that all the peaks of the pureBiOI sample (Figure 1a) coincide with the standard tetragonalBiOI pha 哪里有做XRD和XPS实验? 外文翻译,求高人帮忙翻译一下!急!谢谢!The thermal behaviour of TiO2-WO3-V2O5 catalysts with various vanadia contents (1, 2 and 3 wt.% V2O5) was investigatedusing X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spe 哪里可以做xrd测试和xps测试,急求xrd和xps测试! 纤维测XRD和XPS如何制样英语翻译Abstract：The properties of the passive film formed on 2205 stainless stee1 in acetic acid at high temperature that contained chlorideions were studied by atomic absorption spectrometry(AAS),X—ray photoelectron spectroscopy(XPS),and el XPS & XRD 能测出物质什么信息,怎么分析测出来的图谱呢? 英语翻译6 ConclusionBased upon hardness testing,XRD analysis and microstructural characterization of the weld overlay surfacing,the following can be concluded:(1) Hardfacing is the most versatile process to improve the life of the worn out compon 英语翻译句子如下：An artifact of the sample preparation for XPS analysis was considered,but various procedures gave the same result.重点在前半句,XPS为专有名词--X射线光电子能谱求英化达人翻译哪里有做XRD和XPS实验ITO导电薄膜做XRD和XPS实验,请问南京哪里可以做还有ITO导电薄膜金相实验,最好可以一起做,谢谢! TEM,EDS ,SEM,FE-SEM,STM,AFM,XRD,XPS,FT-IR,UV-VISQ全称和中文名称是什么呀? 英语翻译The X-ray diffraction (XRD) patterns were recordedon a X-ray power diffractometer using Cu Ka radiation(0.15418 nm) (PANalytical Co.X’pert PRO,Netherlands) operated under a voltage of 40 kV and acurrent of 40 mA. 英语翻译3.Results anddiscussion3.1.Kineticsof PU,XPS and EPS degradationThe TG and DTGresults of PU,XPS and EPS under various heating rates (5,10,15,20 ◦C/min)in a nitrogen environment are presented in Figs.1–3,respectively.There are many 英语翻译During thethermal degradation of XPS,the activation energy increases before a= 0.25 andthen the value stabilizes in the range of 220–230 kJ·mol−1.Through theentire process,the E values of XPS are always smaller than that of EPS a 英语翻译4.ConclusionA sol–gel,spray-drying method was used to prepareLiMn2O4 powder.Via DTA,TGA,IR,XRD and SEManalysis,it was shown that the structure and morphologyof LiMn2O4 powder were strongly affected by thespray speed and the heat treatme 英语翻译如题：the significance of changes in the structure is decreasing with the total amount of foreign oxides in the sample.the changes in XRD pattern and lattice parameters that are induced by Fe2O3 decrease with the total amount of doped 英语翻译As per Atamert and Bhadeshia [19] Si is ferrite stabilizer,it retains Cr in the matrix.However in XRD research Cr is precipitated in presence of high amount of Si.This is contradictory to results of Atamert and Bhadeshia.The reason may be 英语翻译the ( ) ( ) ( ) and ( ) ( ) ( )